data_STO

#**************************************************************************
#
# CIF taken from the IZA-SC Database of Zeolite Structures
# Ch. Baerlocher and L.B. McCusker
# Database of Zeolite Structures: http://www.iza-structure.org/databases/ 
#
# The atom coordinates and the cell parameters were optimized with DLS76
# assuming a pure SiO2 composition.
#
#**************************************************************************

_cell_length_a                  29.8860(0)
_cell_length_b                   8.3900(0)
_cell_length_c                  24.7310(0)
_cell_angle_alpha               90.0000(0)
_cell_angle_beta               105.0480(0)
_cell_angle_gamma               90.0000(0)

_symmetry_space_group_name_H-M     'P 2/m'
_symmetry_Int_Tables_number         10
_symmetry_cell_setting             monoclinic

loop_
_symmetry_equiv_pos_as_xyz
'+x,+y,+z'
'-x,+y,-z'
'-x,-y,-z'
'+x,-y,+z'

loop_
_atom_site_label
_atom_site_type_symbol
_atom_site_fract_x
_atom_site_fract_y
_atom_site_fract_z
    O1    O     0.1272    0.0000    0.1995
    O2    O     0.0072    0.2693    0.1761
    O3    O     0.0534    0.5000    0.2384
    O4    O     0.2061    0.0000    0.0239
    O5    O     0.7588    0.2305    0.1632
    O6    O     0.8296    0.2066    0.2515
    O7    O     0.8424    0.2966    0.1545
    O8    O     0.8196    0.0000    0.1691
    O9    O     0.9446    0.2047    0.2303
   O10    O     0.9610    0.0000    0.1567
   O11    O     0.8393    0.2023    0.0519
   O12    O     0.8599    0.5000    0.0818
   O13    O     0.1929    0.5000    0.1338
   O14    O     0.9191    0.2710    0.1226
   O15    O     0.7508    0.2455    0.0052
   O16    O     0.1646    0.2094    0.1453
   O17    O     0.0972    0.2948    0.1900
   O18    O     0.1886    0.2890    0.0538
   O19    O     0.7505    0.2138    0.3366
   O20    O     0.1793    0.2293    0.2551
   O21    O     0.1697    0.2975    0.3556
   O22    O     0.1797    0.0000    0.3275
   O23    O     0.0641    0.2034    0.2738
   O24    O     0.0458    0.0000    0.3465
   O25    O     0.1682    0.2056    0.4570
   O26    O     0.1466    0.5000    0.4247
   O27    O     0.2126    0.0000    0.5321
   O28    O     0.7867    0.5000    0.3551
   O29    O     0.8777    0.0000    0.3240
   O30    O     0.0017    0.2734    0.3277
   O31    O     0.9521    0.5000    0.2668
   O32    O     0.8408    0.2512    0.3592
   O33    O     0.9115    0.2847    0.3152
   O34    O     0.7418    0.2316    0.5015
   O35    O     0.7979    0.2955    0.4382
   O36    O     0.0901    0.2663    0.3815
   O37    O     0.6706    0.1971    0.1589
   O38    O     0.5944    0.2877    0.1842
   O39    O     0.6570    0.5000    0.1773
   O40    O     0.5591    0.0000    0.1816
   O41    O     0.6956    0.2985    0.0704
   O42    O     0.6975    0.5000    0.9893
   O43    O     0.3256    0.2047    0.2321
   O44    O     0.3043    0.5000    0.1990
   O45    O     0.4149    0.2142    0.1179
   O46    O     0.4494    0.5000    0.1440
   O47    O     0.3498    0.0000    0.1140
   O48    O     0.7105    0.0000    0.1032
   O49    O     0.2521    0.2619    0.1495
   O50    O     0.3354    0.3011    0.1350
   O51    O     0.4446    0.2969    0.2235
   O52    O     0.3393    0.2158    0.0345
   O53    O     0.5042    0.2499    0.1629
   O54    O     0.2500    0.1976    0.3431
   O55    O     0.6745    0.2978    0.2609
   O56    O     0.6705    0.2184    0.3622
   O57    O     0.6871    0.0000    0.2939
   O58    O     0.5572    0.1958    0.2640
   O59    O     0.5565    0.0000    0.3467
   O60    O     0.6516    0.2400    0.4594
   O61    O     0.6549    0.5000    0.4008
   O62    O     0.6896    0.0000    0.5239
   O63    O     0.2728    0.5000    0.3600
   O64    O     0.3479    0.0000    0.3150
   O65    O     0.4976    0.2393    0.3245
   O66    O     0.4473    0.5000    0.3056
   O67    O     0.3316    0.2988    0.3351
   O68    O     0.4072    0.2218    0.3052
   O69    O     0.3134    0.2846    0.4334
   O70    O     0.5864    0.2949    0.3676
    T1    Si    0.8651    0.3174    0.1026
    T2    Si    0.7989    0.1842    0.9949
    T3    Si    0.1437    0.3168    0.4046
    T4    Si    0.7940    0.3150    0.3724
    T5    Si    0.6492    0.3198    0.1954
    T6    Si    0.7012    0.3154    0.0076
    T7    Si    0.3599    0.1822    0.1004
    T8    Si    0.6957    0.1830    0.3134
    T9    Si    0.6408    0.3145    0.3973
   T10    Si    0.3532    0.1819    0.2968
   T11    Si    0.2919    0.3197    0.3677
   T12    Si    0.0555    0.3171    0.2196
   T13    Si    0.9579    0.1857    0.1716
   T14    Si    0.1996    0.3151    0.1204
   T15    Si    0.1423    0.1836    0.1973
   T16    Si    0.1946    0.1817    0.3204
   T17    Si    0.9525    0.3157    0.2851
   T18    Si    0.8649    0.1854    0.3124
   T19    Si    0.7898    0.1833    0.4877
   T20    Si    0.0505    0.1855    0.3324
   T21    Si    0.7089    0.1815    0.1238
   T22    Si    0.3043    0.3174    0.1790
   T23    Si    0.3074    0.1880    0.4873
   T24    Si    0.8128    0.1831    0.1847
   T25    Si    0.4534    0.3154    0.1623
   T26    Si    0.5536    0.1832    0.1982
   T27    Si    0.4492    0.3147    0.2894
   T28    Si    0.5493    0.1822    0.3258