Database of Zeolite Structures
 
Framework Type -ITV
Powder Diffraction Pattern for ITQ-37
Input Parameters
  Wavelength:  or
  2θ range:
  Step size:
  Polarization factor:
  Background:
  Reference peak is
    peak closest to °2θ
    reflection (hkl)
       scaled to
  Intensity axis:
     
Peak shape
  Pseudo-Voigt: (1-n)Gaussian + n Lorentzian
  FWHM = sqrt (U + V tan θ + W tan2θ)
  Mixing parameter (n): %
  Peak range: FWHM
  Peak width:
       set UVW at: U =   V =   W =
       Calculate UVW such that FWHM =
    FWHM =
       FWHM =
   
Select Output
 
List hkl and intensity
List powder pattern
plot powder pattern
Crystal Data
  Space Group: P 41 3 2   (# 213)   
  Cell parameters: a = 26.5126 Å b = 26.5126Å c = 26.5126 Å
    α = 90° β = 90° γ = 90 °
  Chemical Formula |TEDATD+2 (H2O)10.5| [Ge80Si112O368OH32]--ITV
TEDATD+2 = C22H40N2+2
= 4,4,10,10-Tetraethyl-1,14-dimethyl-4,10-diazoniatetracyclo[5.5.2.02,6.08,12]tetradec-13-ene   (stick drawing)
  Refinement:
  Reference: Sun, J., Bonneau, C., Cantin, A., Corma, A., Díaz-Cabañas, M.J., Moliner, M., Zhang, D., Li, M. and Zou, X.
Nature, 458, 1154-1157 (2009)
  Atomic Coordinates:          
   
Atom
Form Factor
x
y
z
PP
B(iso)
   
  Si2
Ge
0.0467 0.1615 0.0481 0.331 1.067
  Si2
Ge
0.0467 0.1615 0.0481 0.331 1.067
  Si3
Ge
0.1651 0.1643 0.0473 0.311 1.067
  Si3
Ge
0.1651 0.1643 0.0473 0.311 1.067
  Si4
Ge
0.1663 0.1663 0.1663 0.228 1.067
  Si4
Ge
0.1663 0.1663 0.1663 0.228 1.067
  Si5
Ge
0.238 0.238 0.238 0.192 1.067
  Si5
Ge
0.238 0.238 0.238 0.192 1.067
  Si6
Ge
0.248 0.2423 0.0076 0.265 1.067
  Si6
Ge
0.248 0.2423 0.0076 0.265 1.067
  Si7
Ge
0.1992 0.3348 0.0614 0.231 1.067
  Si7
Ge
0.1992 0.3348 0.0614 0.231 1.067
  Si8
Ge
0.0785 0.3302 0.0655 0.264 1.067
  Si8
Ge
0.0785 0.3302 0.0655 0.264 1.067
  Si9
Ge
0.0789 0.4501 0.0705 0.497 1.067
  Si9
Ge
0.0789 0.4501 0.0705 0.497 1.067
  Si1
Si
0.0453 0.0453 0.0453 0.021 1.067
  Si1
Si
0.0453 0.0453 0.0453 0.021 1.067
  Si10
Si
0.2005 0.4519 0.0622 0.032 1.067
  Si10
Si
0.2005 0.4519 0.0622 0.032 1.067
  O1
O
0.0073 0.0073 0.0073 1 2.72
  O2
O
0.0201 0.1053 0.0427 1 2.72
  O3
O
0.0364 0.1833 0.1054 1 2.72
  O4
O
0.1056 0.1665 0.0302 1 2.72
  O5
O
0.0148 0.1979 0.0079 1 2.72
  O6
O
0.1751 0.1808 0.1065 1 2.72
  O7
O
0.2022 0.2022 0.2022 1 2.72
  O8
O
0.1997 0.2025 0.0117 1 2.72
  O9
O
0.2311 0.2999 0.0205 1 2.72
  O10
O
0.2186 0.322 0.1191 1 2.72
  O11
O
0.2187 0.3915 0.0471 1 2.72
  O12
O
0.139 0.3248 0.0526 1 2.72
  O13
O
0.0434 0.2949 0.0279 1 2.72
  O14
O
0.0658 0.3157 0.125 1 2.72
  O15
O
0.0618 0.3903 0.06 1 2.72
  O16
O
0.0455 0.4898 0.0336 1 2.72
  O17
O
0.137 0.4594 0.0502 1 2.72
  O18
O
0.2151 0.4651 0.125 1 2.72
  O19
O
0.2329 0.4952 0.0234 1 2.72
  O31
O
0.432 0.676 0.012 1.3 7.67
  O32
O
0.8175 0.1919 0.6133 1.3 7.67
  O33
O
0.3569 0.7811 0.379 1.3 7.67
  O34
O
0.615 0.8537 0.4634 1.3 7.67
  F1
F
0.1058 0.1058 0.1058 1 7.67
  F2
F
0.1395 0.3895 0.125 1 7.67
  C1
C
0.6838 0.0575 0.1764 1.3 7.67
  C2
C
0.622 0.3984 0.1658 1.3 7.67
  C3
C
0.5537 0.2994 0.3811 1.3 7.67
  C4
C
0.0981 0.3486 0.349 1.3 7.67
  C5
C
0.6047 0.3281 0.2618 1.3 7.67
  C6
C
0.0611 0.182 0.9029 1.3 7.67
  C7
C
0.8554 0.095 0.4308 1.3 7.67
  C8
C
0.868 0.1983 0.5136 1.3 7.67
  C9
C
0.0964 0.4892 0.4008 1.3 7.67
  C10
C
0.5649 0.1381 0.3951 1.3 7.67
  C11
C
0.8017 0.1099 0.295 1.3 7.67
  C12
C
0.0785 0.0509 0.9212 1.3 7.67