Database of Zeolite Structures
 
Framework Type TUN
Powder Diffraction Pattern for TNU-9
Input Parameters
  Wavelength:  or
  2θ range:
  Step size:
  Polarization factor:
  Background:
  Reference peak is
    peak closest to °2θ
    reflection (hkl)
       scaled to
  Intensity axis:
     
Peak shape
  Pseudo-Voigt: (1-n)Gaussian + n Lorentzian
  FWHM = sqrt (U + V tan θ + W tan2θ)
  Mixing parameter (n): %
  Peak range: FWHM
  Peak width:
    set UVW at: U =   V =   W =
    FWHM =
    FWHM =
  FWHM =
   
Select Output
 
List hkl and intensity
List powder pattern
plot powder pattern
Crystal Data
  Space Group: C 1 2/m 1   (# 12)   
  Cell parameters: a = 28.204 Å b = 20.043Å c = 19.48 Å
    α = 90° β = 92.3° γ = 90 °
  Chemical Formula |H9.3 | [Al9.3Si182.7O384]-TUN
  Refinement:
  Comment: unique axis b, cell choice 1
  Reference: Gramm, F., Baerlocher, Ch., McCusker, L.B., Warrender, S.J., Wright, P.A., Han, B., Hong, S.B., Liu, Z., Ohsuna, T. and Terasaki, O.
Nature, 444, 79-81 (2006)
  Atomic Coordinates:          
   
Atom
Form Factor
x
y
z
PP
B(iso)
   
  Si1
Si
0.1057 0.1895 0.7052 1.8 1
  Si2
Si
0.0037 0.3059 0.1448 1.8 1
  Si3
Si
0.1505 0.1869 0.1668 1.8 1
  Si4
Si
0.0903 0.1217 0.9281 1.8 1
  Si5
Si
0.106 0.3068 0.0843 1.8 1
  Si6
Si
0.003 0.0777 0.143 1.8 1
  Si7
Si
0.1028 0.4253 0.7126 1.8 1
  Si8
Si
0.151 0.4229 0.1722 1.8 1
  Si9
Si
0.1009 0.0767 0.078 1.8 1
  Si10
Si
0.2532 0.3783 0.2245 1.8 1
  Si11
Si
0.1445 0.0786 0.7995 1.8 1
  Si12
Si
0.1645 0.3773 0.4393 1.8 1
  Si13
Si
0.1 0.3797 0.3085 1.8 1
  Si14
Si
0.2392 0.0775 0.62 1.8 1
  Si15
Si
0.0004 0.4233 0.2498 1.8 1
  Si16
Si
-0.0021 0.188 0.2534 1.8 1
  Si17
Si
0.2358 0.3101 0.618 1.8 1
  Si18
Si
0.1436 0.3084 0.8004 1.8 1
  Si19
Si
0.1655 0.2182 0.4331 1.8 1
  Si20
Si
0.1002 0.2215 0.3047 1.8 1
  Si21
Si
0.1641 0.4237 0.5858 1.8 1
  Si22
Si
0.0875 0.2788 0.9289 1.8 1
  Si23
Si
0.1672 0.1911 0.5794 1.8 1
  Si24
Si
0.2534 0.2186 0.2244 1.8 1
  O1
O
0.0401 0.091 0.91 2.2 1
  O2
O
0.0883 0.2001 0.936 2.2 1
  O3
O
0.1247 0.106 0.869 2.2 1
  O4
O
0.1097 0.089 -0.0018 2.2 1
  O5
O
0.1259 0.205 0.631 2.2 1
  O6
O
0.125 0.247 0.755 2.2 1
  O7
O
0.125 0.119 0.733 2.2 1
  O8
O
0.0484 0.19 0.701 2.2 1
  O9
O
0.0477 0.095 0.098 2.2 1
  O10
O
0.113 0 0.095 2.2 1
  O11
O
0.1377 0.118 0.127 2.2 1
  O12
O
0.1997 0.093 0.808 2.2 1
  O13
O
0.134 0 0.797 2.2 1
  O14
O
0.1221 0.308 0.874 2.2 1
  O15
O
0.1056 0.306 0.0019 2.2 1
  O16
O
0.0353 0.306 0.917 2.2 1
  O17
O
0.2065 0.189 0.187 2.2 1
  O18
O
0.3 0.191 0.19 2.2 1
  O19
O
0.251 0.197 0.3024 2.2 1
  O20
O
0.2554 0.2983 0.223 2.2 1
  O21
O
0.0534 0.294 0.11 2.2 1
  O22
O
0.994 0.247 0.198 2.2 1
  O23
O
0 0.377 0.183 2.2 1
  O24
O
0.1387 0.247 0.114 2.2 1
  O25
O
0.1254 0.189 0.24 2.2 1
  O26
O
0.127 0.378 0.111 2.2 1
  O27
O
0.002 0 0.161 2.2 1
  O28
O
0.001 0.118 0.214 2.2 1
  O29
O
0.1234 0.413 0.639 2.2 1
  O30
O
0.047 0.409 0.709 2.2 1
  O31
O
0.13 0.379 0.767 2.2 1
  O32
O
0.114 0.5 0.74 2.2 1
  O33
O
0.129 0.411 0.247 2.2 1
  O34
O
0.145 0.5 0.149 2.2 1
  O35
O
0.2073 0.407 0.181 2.2 1
  O36
O
0.248 0.4 0.3028 2.2 1
  O37
O
0.1725 0.2975 0.44 2.2 1
  O38
O
0.2152 0.409 0.424 2.2 1
  O39
O
0.1453 0.403 0.5104 2.2 1
  O40
O
0.1238 0.397 0.383 2.2 1
  O41
O
0.0457 0.407 0.301 2.2 1
  O42
O
0.1027 0.3006 0.296 2.2 1
  O43
O
0.1945 0.121 0.593 2.2 1
  O44
O
0.225 0 0.615 2.2 1
  O45
O
-0.001 0.5 0.224 2.2 1
  O46
O
0.0456 0.197 0.301 2.2 1
  O47
O
0.208 0.379 0.611 2.2 1
  O48
O
0.2852 0.318 0.581 2.2 1
  O49
O
0.2039 0.252 0.584 2.2 1
  O50
O
0.1447 0.191 0.5028 2.2 1
  O51
O
0.1255 0.199 0.376 2.2 1
  O52
O
0.182 0.5 0.585 2.2 1